構造用碳素鋼 SC材系列
鋼種 記號 |
化學成分 % | ||||
C | Si | Mn | P | S | |
S10C | 0.08~0.13 | 0.15~0.35 | 0.30~0.60 | <0.030 | <0.035 |
S12C S15C |
0.10~0.15 0.13~0.18 |
0.15~0.35 | 0.30~0.60 | <0.030 | <0.035 |
S17C S20C |
0.15~0.20 0.18~0.23 |
0.15~0.35 | 0.30~0.60 | <0.030 | <0.035 |
S22C S25C |
0.20~0.25 0.22~0.28 |
0.15~0.35 | 0.30~0.60 | <0.030 | <0.035 |
S28C S30C |
0.25~0.31 0.27~0.33 |
0.15~0.35 | 0.30~0.90 | <0.030 | <0.035 |
S33C S35C |
0.30~0.36 0.32~0.38 |
0.15~0.35 | 0.30~0.90 | <0.030 | <0.035 |
S38C S40C |
0.35~0.41 0.37~0.43 |
0.15~0.35 | 0.30~0.90 | <0.030 | <0.035 |
S43C S45C |
0.40~0.46 0.42~0.48 |
0.15~0.35 | 0.30~0.90 | <0.030 | <0.035 |
S48C S50C |
0.45~0.51 0.47~0.53 |
0.15~0.35 | 0.30~0.90 | <0.030 | <0.035 |
S53C S55C |
0.50~0.56 0.52~0.58 |
0.15~0.35 | 0.30~0.90 | <0.030 | <0.035 |
S58C | 0.55~0.61 | 0.15~0.35 | 0.30~0.90 | <0.030 | <0.035 |
S09CK | 0.07~0.12 | 0.15~0.35 | 0.30~0.60 | <0.025 | <0.025 |
S15CK | 0.13~0.18 | 0.15~0.35 | 0.30~0.60 | <0.025 | <0.025 |
S20CK | 0.18~0.23 | 0.15~0.35 | 0.30~0.60 | <0.025 | <0.025 |
熱處理條件
鋼種記號 | 熱處理 ℃ | |||
正常化 | 退火 | 淬火 | 回火 | |
S10C | 900~950 空冷 | 約 900 爐冷 | ||
S12C S15C |
880~930 空冷 | 約 880 Furnace coole | ||
S17C S20C |
870~920 空冷 | 約 860 爐冷 | ||
S22C S25C |
860~910 空冷 | 約 850 爐冷 | ||
S28C S30C |
850~900 空冷 | 約 840 爐冷 | 850~900 水淬 | 550~650 急冷 |
S33C S35C |
840~890 空冷 | 約 830 爐冷 | 840~890 水淬 | 550~650 急冷 |
S38C S40C |
830~880 空冷 | 約 820 爐冷 | 830~880 水淬 | 550~650 急冷 |
S43C S45C |
820~870 空冷 | 約 810 爐冷 | 820~870 水淬 | 550~650 急冷 |
S48C S50C |
810~860 空冷 | 約 800 爐冷 | 810~860 水淬 | 550~650 急冷 |
S53C S55C |
800~850 空冷 | 約 790 爐冷 | 800~850 水淬 | 550~650 急冷 |
S58C | 800~850 空冷 | 約 790 爐冷 | 800~850 水淬 | 550~650 急冷 |
S09CK | 900~950 空冷 | 約 900 爐冷 |
1次880~920油(水)淬 2次750~800 水淬 |
150~200 空冷 |
S15CK | 880~930 空冷 | 約 880 爐冷 |
1次870~920油(水)淬 2次750~800 水淬 |
150~200 空冷 |
S20CK | 870~920 空冷 | 約 860 爐冷 |
1次870~920油(水)淬 2次750~800 水淬 |
150~200 空冷 |